方法对比
并排查看您选择的方法；存在差异的行会高亮显示。
| 弯曲强度和弹性模量× | 木材收缩× | |
|---|---|---|
| 领域 | 林学 | 林学 |
| 方法族 | Process / pipeline | Process / pipeline |
| 起源年份 | 1950 | 1950 |
| 提出者≠ | ASTM International | Carl Skaar |
| 类型≠ | mechanical test | moisture response test |
| 开创性文献 | ASTM D143-19. (2019). Standard test methods for small clear specimens of timber. ASTM International. link ↗ | ASTM D143-19. (2019). Standard test methods for small clear specimens of timber. ASTM International. link ↗ |
| 别名≠ | MOR, MOE, bending strength | dimensional change, anisotropic shrinkage |
| 相关≠ | 3 | 2 |
| 摘要≠ | The Modulus of Rupture (MOR) and Modulus of Elasticity (MOE) are standardized measures of wood mechanical properties determined through static bending tests. MOR quantifies the maximum bending stress wood can withstand before failure; MOE measures stiffness (resistance to bending). These are fundamental properties used for wood grading, structural design, and assessment of wood quality and species suitability for applications requiring strength or stiffness. | Wood shrinkage is the dimensional change that occurs as wood loses moisture from green (freshly felled) to oven-dry condition. Wood shrinks anisotropically: tangentially (along growth rings) more than radially (from center to edge), and both more than longitudinally (along the grain). Measuring shrinkage percentages is essential for understanding wood drying behavior, predicting checking and warping, and selecting materials for applications sensitive to dimensional change (flooring, cabinetry, musical instruments). |
| ScholarGate数据集 ↗ |
|
|